INEOS LDPE M21E730

About
LDPE ionomer for film products Benefits & Features M21E730 is an ionomer, produced by the neutralization of an ethylene methacrylic acid (MAA) copolymer. It offers the following properties: Very high impact strength Exceptional drawdown Very low resistance to tear propagation in both machine and transverse directions Good optical properties Applications M21E730 has been developed for easy tear film applications such as collation shrink film, envelopes, overwrap and bags. It can be blended or co-extruded with other types of polyethylene to tailor performance.&&

About

LDPE ionomer for film products Benefits & Features M21E730 is an ionomer, produced by the neutralization of an ethylene methacrylic acid (MAA) copolymer. It offers the following properties: Very high impact strength Exceptional drawdown Very low resistance to tear propagation in both machine and transverse directions Good optical properties Applications M21E730 has been developed for easy tear film applications such as collation shrink film, envelopes, overwrap and bags. It can be blended or co-extruded with other types of polyethylene to tailor performance.&&

Product Description
Supplier	INEOS
Generic	LDPE
Material Status	Commercial: Active
Features	High impact resistance,Good dissection,Optical performance,Low density
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.933	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	0.50	g/10min	ISO 1133
Methacrylic Acid Content	1.7	%	Internal Method

film	Nominal value	Unit	Test method
film thickness
test	50	µm
Tensile modulus			ISO 1184
1% secant, MD, 50 µ m, blow molded film	165	MPa	ISO 1184
1% secant, TD, 50 µ m, blow molded film	175	MPa	ISO 1184
tensile strength			ISO 1184
MD, yield, 50 µ m, blow molded film	11.0	MPa	ISO 1184
TD, yield, 50 µ m, blow molded film	10.0	MPa	ISO 1184
tensile strength			ISO 1184
MD, fracture, 50 µ m, blow molded film	28.0	MPa	ISO 1184
TD, fracture, 50 µ m, blow molded film	29.0	MPa	ISO 1184
Tensile strain			ISO 1184
MD, fracture, 50 µ m, blow molded film	200	%	ISO 1184
TD, fracture, 50 µ m, blow molded film	400	%	ISO 1184
Drop hammer impact
50 µ m, blow molded film	750	g	ASTM D1709-A
tear strength
TD, 50 µ m, blow molded film	54	g	ASTM D1922
MD, 50 µ m, blow molded film	48	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	92.0	℃	ISO 306/A

optical performance	Nominal value	Unit	Test method
gloss
45 °, 50.0 µ m, blow molded film	60		ASTM D2457
Haze
50 µ m, blow molded film	9.0	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	160 to 200	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.