| About |
|---|
| LLDPE for film products Applications LL6130AA is particularly suitable for high performance cast stretch film applications, in particular as a core layer in co-extruded structures. Characteristics LL6130AA s a linear low density polyethylene copolymer containing hexene (C6) as the co-monomer. It offers the following properties: High output rates Excellent overall film appearance and surface finish Very good puncture resistance&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Inoxidizability,Low density,Copolymer,Puncture Resistant,Hexene copolymers |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ISO 1183/D |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Tensile modulus | ISO 1184 | ||
| 1% secant, MD, 20 µ m | 90.0 | MPa | ISO 1184 |
| 1% secant, TD, 20 µ m | 110 | MPa | ISO 1184 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 20 µ m | 33.0 | MPa | ISO 527-3 |
| TD, fracture, 20 µ m | 25.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 1184 | ||
| MD, fracture, 20 µ m | 600 | % | ISO 1184 |
| TD, fracture, 20 µ m | 750 | % | ISO 1184 |
| Drop hammer impact | |||
| 20 µm | 160 | g | ASTM D1709-A |
| tear strength | |||
| TD，20 µm | 560 | g | ASTM D1922 |
| MD，20 µm | 240 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，20 µm | 93 | ASTM D2457 | |
| Haze | |||
| 20 µm | 1.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | 30.0 | Ncm/µ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 240 to 280 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |