INEOS LLDPE LL6608AF

About
LLDPE film products Applications LL6608AF has been developed for lean and rich blend blown film applications, such as rigid layers in co-extrusion, carrier bags, refuse sacks and liners. This grade is also recommended for artificial grass applications Benefits and Features LL6608AF is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties: Optimum balance between stiffness and film strength Good optical properties Good bubble stability Excellent sealability and hot-tack strength If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.&&

About

LLDPE film products Applications LL6608AF has been developed for lean and rich blend blown film applications, such as rigid layers in co-extrusion, carrier bags, refuse sacks and liners. This grade is also recommended for artificial grass applications Benefits and Features LL6608AF is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties: Optimum balance between stiffness and film strength Good optical properties Good bubble stability Excellent sealability and hot-tack strength If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.&&

Product Description
Supplier	INEOS
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Good heat sealing,Optical performance,Inoxidizability,Low density,Copolymer,Hexene copolymers
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.928	g/cm³	ISO 1183/D
Melt Flow Rate
190℃，2.16kg	0.90	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	38	µm
Tensile modulus
1% secant, 38 µ m, blow molded film	290	MPa	ISO 1184
tensile strength			ISO 527-3
MD, yield, 38 µ m, blow molded film	14.0	MPa	ISO 527-3
TD, yield, 38 µ m, blow molded film	16.0	MPa	ISO 527-3
tensile strength			ISO 527-3
MD, fracture, 38 µ m, blow molded film	50.0	MPa	ISO 527-3
TD, fracture, 38 µ m, blow molded film	35.0	MPa	ISO 527-3
Tensile strain			ISO 1184
MD, fracture, 38 µ m, blow molded film	750	%	ISO 1184
TD, fracture, 38 µ m, blow molded film	900	%	ISO 1184
Drop hammer impact
38 µ m, blow molded film	170	g	ASTM D1709-A
tear strength
MD, 38 µ m, blow molded film	110	g	ASTM D1922
Elmandorf tear strength
TD, 38 µ m, blow molded film	650	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	116	℃	ISO 306/A

optical performance	Nominal value	Unit	Test method
gloss
45 °, 38 µ m, blow molded film	56		ASTM D2457
Haze
38 µ m, blow molded film	11	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	190 to 230	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.