| About |
|---|
| LLDPE film products Applications LL6608LJ has been developed for the production of mailing film, carrier, bread and produce bags. Benefits and Features LL6608LJ is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties: Optimum balance between stiffness and film strength Good optical properties Good bubble stability Excellent sealability and hot-tack strength LL6608LJ offers high slip film with easy opening properties when used pure in the thickness range 30 to 70 µm. Addition of other polymers, masterbatch and pigments, or the use of other thicknesses may alter film slip and antiblock performance. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good heat sealing,Smoothness,Optical performance,High anti-blocking,Inoxidizability,Low density,Copolymer,Hexene copolymers |
| Availabilitys | Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.929 | g/cm³ | ISO 1183/D |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | < 0.20 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| Tensile modulus | |||
| 1% secant, 38 µ m, blow molded film | 290 | MPa | ISO 1184 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 38 µ m, blow molded film | 14.0 | MPa | ISO 527-3 |
| TD, yield, 38 µ m, blow molded film | 16.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 38 µ m, blow molded film | 50.0 | MPa | ISO 527-3 |
| TD, fracture, 38 µ m, blow molded film | 35.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 1184 | ||
| MD, fracture, 38 µ m, blow molded film | 750 | % | ISO 1184 |
| TD, fracture, 38 µ m, blow molded film | 900 | % | ISO 1184 |
| Drop hammer impact | |||
| 38 µ m, blow molded film | 170 | g | ASTM D1709-A |
| tear strength | |||
| MD, 38 µ m, blow molded film | 110 | g | ASTM D1922 |
| Elmandorf tear strength | |||
| TD, 38 µ m, blow molded film | 650 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 116 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 38 µ m, blow molded film | 57 | ASTM D2457 | |
| Haze | |||
| 38 µ m, blow molded film | 12 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Silica |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |