| About |
|---|
| H14A-00 is an antistatic polypropylene homopolymer designed for injection molding applications such as consumer products, housewares, medical packaging, and rigid packaging. The grade benefits from fast cycle times, high flow rate, and a low static charge. This material has been recognized by UL for sustained use at 65 C and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High liquidity,Quick molding cycle,Food contact compliance,Antistatic property,Homopolymer,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.906 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 14 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，Area | 2.40 | kJ/m² | ASTM D256 |
| 23℃ | 27 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 92.2 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance, 3.00 mm | 65.0 | ℃ | UL 746 |
| Strength mechanical performance, 3.00 mm | 65.0 | ℃ | UL 746 |
| Impact mechanical performance, 3.00 mm | 65.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 93 | ASTM D2457 | |
| Haze | |||
| 1270 µm | 82 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 17.7 | MPa | ASTM D638 |
| yield | 34.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 200 | % | ASTM D638 |
| yield | 9.0 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1630 | MPa | ASTM D790-A |
| Rockwell hardness | |||
| R-level | 103 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |