| About |
|---|
| L12Z-01 is a nucleated, antistated polypropylene impact copolymer with an excellent balance of stiffness and impact and fast injection cycles. It is specially formulated to help provide superior gloss in applications such as consumer products, housewares, and toys. This material has been recognized by UL for sustained use at 65°C and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Nucleation,Quick molding cycle,Food contact compliance,Antistatic property,Impact copolymer,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.903 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| Area | ASTM D256 | ||
| -20℃ | 48 | J/m | ASTM D256 |
| 23℃ | 180 | J/m | ASTM D256 |
| -20℃ | 5.00 | kJ/m² | ASTM D256 |
| 23℃ | 18.0 | kJ/m² | ASTM D256 |
| Instrumented Impact，Ductility | ASTM D3763 | ||
| -20℃ | Mixed | ASTM D3763 | |
| 23℃ | Ductile | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 53.9 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 104 | ℃ | ASTM D648 |
| Vicat Softening Temp | 149 | ℃ | ASTM D1525 |
| Relative temperature index | |||
| Electrical performance, 1.50 mm | 65.0 | ℃ | UL 746 |
| Strength mechanical performance, 1.50 mm | 65.0 | ℃ | UL 746 |
| Impact mechanical performance, 1.50 mm | 65.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 81 | ASTM D2457 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 17.2 | MPa | ASTM D638 |
| yield | 26.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 160 | % | ASTM D638 |
| yield | 7.0 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1300 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 84 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.050 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |