| About |
|---|
| N05U-00 is an extrusion-grade nucleated impact copolymer polypropylene resin designed for fiber optic buffer tube applications in the protection of glass fibers. N05U-00 has an excellent impact/stiffness property balance and provides the high compression strength required to meet the Bellcore GR-20-CORE standard (Generic Requirements for Optical Fiber and Fiber Optic Cable).&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Nucleation,Good compressive strength,Impact copolymer |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.907 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| Area | ASTM D256 | ||
| -20℃ | 64 | J/m | ASTM D256 |
| 23℃ | 400 | J/m | ASTM D256 |
| -20℃ | 6.20 | kJ/m² | ASTM D256 |
| 23℃ | 38.7 | kJ/m² | ASTM D256 |
| Instrumented Impact，Ductility | ASTM D3763 | ||
| -20℃ | Ductile | ASTM D3763 | |
| 23℃ | Ductile | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 57.2 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 106 | ℃ | ASTM D648 |
| Vicat Softening Temp | 151 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 64 | ASTM D2457 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 19.2 | MPa | ASTM D638 |
| yield | 26.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 130 | % | ASTM D638 |
| yield | 5.2 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1490 | MPa | ASTM D790-A |
| Rockwell hardness | |||
| R-level | 89 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |