| About |
|---|
| BPD2167 is an unstabilised low density thermoplastic polyethylene. It is designed for use in “Câble de façade” application and one step silane crosslinking insulation. A carefully selected carbon black and additives master batch needs to be added to BPD2167 to reach the final “Cable de Façade” formulation. The best performance in terms of homogeneity, aging and anchorage tests is however obtained with the fully formulated black compound BPD8167, to which only the Silane mixture needs to be added.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Crosslinked,Low density |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.20 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 18.0 | MPa | IEC 60811-1-1 |
| Tensile strain | |||
| fracture | > 500 | % | IEC 60811-1-1 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | > 22 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 50 Hz | 2.30 | ASTM D150 | |
| Dissipation factor | |||
| 50 Hz | 4.0E-4 | ASTM D150 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |