| About |
|---|
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| 250℃，10kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.4-0.7 | % | ASTM D955 |
| TD | 0.4-0.7 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 50 mm/min | 580 | kg/cm² | ASTM D638 |
| Fracture, 50 mm/min | 700 | kg/cm² | ASTM D638 |
| Tensile strain | |||
| Fracture, 50 mm/min | 110 | % | ASTM D638 |
| Tensile modulus | |||
| 50 mm/min | 20500 | kg/cm² | ASTM D638 |
| bending strength | |||
| 2.80 mm/min | 800 | kg/cm² | ASTM D790 |
| Bending modulus | |||
| 2.80 mm/min | 20000 | kg/cm² | ASTM D790 |
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa，6.4 mm | 131 | ℃ | ASTM D648 |
| 0.45 MPa，6.4 mm | 139 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 143 | ℃ | ISO R306 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 1/4 | 60 | ASTM D256 | |
| 1/8 | 75 | ASTM D256 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | 额定值 | 单位 | 测试方法 |
| 2.60-3.20 mm | HB | UL 94 | |
| 1.60-2.00 mm | V-2 | UL 94 | |
| Flame retardant level | |||
| 0.8 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |