| About |
|---|
| Infino CF-3200HF是一种聚碳酸酯（PC）产品,含有的填充物为20%玻璃纤维增强材料。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。特性包括:阻燃/额定火焰,通过 ROHS 认证 |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Glass fiber reinforced |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 23 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.50 | % | ASTM D955 |
| TD：3.2 mm | 0.30 to 0.50 | % | ASTM D955 |
| MD：3.2 mm | 0.30 to 0.50 | % | ISO 2577 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃，4mm | 25 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 190 | J/m | ASTM D256 |
| 23℃，4mm | 19 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 141 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 137 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-2 | UL 94 | |
| 3.20 mm | V-1 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 116 | ASTM D785 | |
| R-level | 116 | ISO 2039-2 | |
| tensile strength | |||
| Yield, 5 mm/min | 98.0 | MPa | ASTM D638 |
| yield | 100 | MPa | ISO 527-2/5 |
| Bending modulus | |||
| 2.80 mm/min | 5500 | MPa | ASTM D790 |
| 2 mm/min | 6000 | MPa | ISO 178 |
| bending strength | |||
| 2.80 mm/min | 140 | MPa | ASTM D790 |
| 2 mm/min | 170 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | |||
| 4.0 to 6.0 | hr | ||
| Hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 270 | °C | |
| Barrel middle temperature | 280 to 290 | °C | |
| Barrel front temperature | 300 | °C | |
| Nozzle temperature | 300 | °C | |
| Mold temperature | 80.0 to 120 | °C | |
| Injection pressure | 98.1 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |