| About |
|---|
| Infino HX-4300G is a Polyphthalamide (PPA) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Electrical/Electronic Applications. Characteristics include: Flame Rated Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| – | 1.45 | g/cm³ | ISO 1183 |
| 1.45 | g/cm³ | ASTM D792 | |
| Melt Flow Rate | |||
| 330℃，2.16kg | 25 | g/10min | ISO 1133 |
| 330℃，2.16kg | 25 | g/10min | ASTM D1238 |
| Shrinkage rate | ISO 2577 | ||
| TD：3.2 mm | 0.57 to 0.70 | % | ASTM D955 |
| MD：3.2 mm | 0.45 to 0.55 | % | ASTM D955 |
| TD：3.2 mm | 0.57 to 0.70 | % | ISO 2577 |
| MD：3.2 mm | 0.45 to 0.55 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 8.3 | kJ/m² | ISO 180-1A |
| 23℃，3.2mm | 64 | J/m | ASTM D256 |
| 23℃，6.4mm | 69 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 290 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 290 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 1 | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.4 to 3.0 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8350 | MPa | ASTM D638 |
| Tensile modulus | 9600 | MPa | ISO 527-2/5 |
| tensile strength | |||
| fracture | 170 | MPa | ISO 527-2/5 |
| fracture | 167 | MPa | ASTM D638 |
| yield | 167 | MPa | ASTM D638 |
| yield | 160 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| fracture | 3.0 | % | ISO 527-2/5 |
| Bending modulus | 9810 | MPa | ASTM D790 |
| Bending modulus | 10600 | MPa | ISO 178 |
| bending strength | 216 | MPa | ASTM D790 |
| bending strength | 210 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| R-level | 122 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 120 | °C | |
| Hot air dryer | 120 | °C | |
| Drying time | |||
| — | 4.0 to 6.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 280 to 290 | °C | |
| Barrel middle temperature | 300 to 310 | °C | |
| Barrel front temperature | 320 to 330 | °C | |
| Nozzle temperature | 330 | °C | |
| Mold temperature | 100 to 140 | °C | |
| Injection pressure | 108 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.11 in/min |
| 4. 0.079 in/min |
| 5. Thickness: 4mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |