| About |
|---|
| Infino LB-1010W is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | V-2,Flame Characteristics |
| Availabilitys | North America,Latin America,Asia Pacific,Europe,Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| proportion | 1.26 | ASTM D792 | |
| Melt index | |||
| 250℃，10.0kg | 48 | g/10min | ASTM D1238 |
| Forming shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 372 | J/m | ASTM D256 |
| 23℃，3.2mm | 490 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 18.56kgf/, 6.4mm | 129 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B/50 | 139 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 50mm/min | 2157 | MPa | ASTM D638 |
| tensile strength | |||
| 50mm/min, yield | 52.0 | MPa | ASTM D638 |
| elongation at break | |||
| 50mm/min | 80 | % | ASTM D638 |
| Breaking strength | |||
| 50mm/min | 57.8 | MPa | ASTM D638 |
| bending strength | |||
| 2.8mm/min | 76.5 | MPa | ASTM D790 |
| Bending modulus | |||
| 2.8mm/min | 2059 | MPa | ASTM D790 |
| Rockwell hardness | 120 | R Scale | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | |||
| — | 120 | °C | |
| Hot air dryer | 110 | °C | |
| Drying time | |||
| — | 2.0 to 6.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Temperature at the rear of the barrel | 240 to 250 | °C | |
| Temperature in the middle of the barrel | 260 to 270 | °C | |
| Front temperature of material barrel | 280 to 290 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Mold temperature | 40 to 100 | °C | |
| Injection pressure | 49.0 to 245 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2,0 in/min |
| 3. 0,11 in/min |
| 4. 0,079 in/min |
| 5. Thickness: 4mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |