| About |
|---|
| Infino NH-1015V是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)产品,。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 特性包括: 阻燃/额定火焰 Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0,5VB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| – | 1.17 | g/cm³ | ISO 1183 |
| 1.17 | g/cm³ | ASTM D792 | |
| Melt Flow Rate | |||
| 220℃，10.0kg | 30 | g/10min | ISO 1133 |
| 220℃，10.0kg | 30 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 540 | J/m | ASTM D256 |
| 23℃ | 14 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 4.0 mm | 97.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed, 6.4 mm | 86.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 82.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed, 4.0 mm | 102 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed, 4.0 mm | 94.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 100 | ℃ | ISO 306 |
| B120 | 103 | ℃ | ISO 306/B120 |
| Relative temperature index | |||
| Electrical performance, 1.50 mm | 90.0 | ℃ | UL 746 |
| Strength mechanical performance, 1.50 mm | 90.0 | ℃ | UL 746 |
| Impact mechanical performance, 1.50 mm | 85.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2500 | MPa | ISO 527-2/50 |
| tensile strength | |||
| fracture | 48.0 | MPa | ISO 527-2/50 |
| yield | 64.0 | MPa | ASTM D638 |
| yield | 61.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 45 | % | ISO 527-2/50 |
| Bending modulus | 2400 | MPa | ASTM D790 |
| Bending modulus | 2550 | MPa | ISO 178 |
| bending strength | 87.0 | MPa | ASTM D790 |
| bending strength | 89.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| R-level | 118 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying time | |||
| — | 4.0 to 6.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 220 to 230 | °C | |
| Barrel middle temperature | 240 to 250 | °C | |
| Barrel front temperature | 260 to 270 | °C | |
| Nozzle temperature | 270 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Injection pressure | 98.1 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |