| Infino TK-2046M是一种聚对苯二甲酸环己基二亚甲酯 (PCT)产品,含有的填充物为玻璃纤维增强材料。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 主要特性为:阻燃/额定火焰。 |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | PCT |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | ASTM D955 |
| TD：3.2 mm | 0.50 to 0.80 | % | ASTM D955 |
| TD：2.0 mm | 0.50 to 0.80 | % | ISO 294-4 |
| TD：2.0 mm | 0.50 to 0.80 | % | ISO 294-4 |
| Ash Content | |||
| — | 41 | % | ASTM D5630 |
| — | 41 | % | ISO 3451 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 4800 | MPa | ASTM D638 |
| — | 4200 | MPa | ISO 527-2/10 |
| Tensile strength | |||
| yield | 73.0 | MPa | ASTM D638 |
| yield | 60.0 | MPa | ISO 527-2/10 |
| fracture | 73.0 | MPa | ASTM D638 |
| fracture | 60.0 | MPa | ISO 527-2/10 |
| Tensile strain | |||
| fracture | 2.2 | % | ASTM D638 |
| fracture | 1.6 | % | ISO 527-2/10 |
| Bending modulus | |||
| — | 6400 | MPa | ASTM D790 |
| — | 6900 | MPa | ISO 178 |
| bending strength | |||
| — | 110 | MPa | ASTM D790 |
| — | 105 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.6 | kJ/m² | ISO 179/1eA |
| Notched impact strength of cantilever beam | |||
| -5℃，3.2 mm | 250 | J/m | |
| -5℃，6.4 mm | 190 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 250 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 250 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index (3.20 mm) | YI | ASTM D1925 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | |||
| Hot air dryer | 80 to 100 | °C | |
| Vacuum dryer | 100 | °C | |
| Drying time | |||
| Hot air dryer | 4.0 | hr | |
| Vacuum dryer | 4.0 | hr | |
| Recommended maximum moisture content | 0.060 | % | |
| Temperature at the rear of the barrel | 290 to 300 | °C | |
| Temperature in the middle of the barrel | 300 | °C | |
| Front temperature of material barrel | 305 to 310 | °C | |
| Nozzle temperature | 305 to 310 | °C | |
| Mold temperature | 50 to 60 | °C | |
| Injection pressure | 7.85 to 12.7 | MPa | |
| Back pressure | 7.85 to 12.7 | MPa | |
| Screw speed | 180 to 250 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |