| About |
|---|
| Infino VB-8202G is a Polyphenylene Ether (PPE) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Infino VB-8202G include business/office goods and tanks. Characteristics include: Flame Rated Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | PPO(PPE) |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-1 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| – | 1.22 | g/cm³ | ISO 1183 |
| 1.22 | g/cm³ | ASTM D792 | |
| Melt Flow Rate | |||
| 250℃，10.0kg | 4.0 | g/10min | ASTM D1238 |
| 250℃，10.0kg | 4.0 | g/10min | ISO 1133 |
| Ash Content | |||
| — | 20 | % | ISO 3451 |
| — | 20 | % | ASTM D5630 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 98.0 | MPa | ASTM D638 |
| Bending modulus | 5900 | MPa | ASTM D790 |
| bending strength | 150 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 98 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 135 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-1 | UL 94 | |
| 1.60 mm | V-1 | UL 94 | |
| 3.00 mm | V-1 | UL 94 | |
| 6.00 mm | V-1 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 100 | °C | |
| Hot air dryer | 100 | °C | |
| Drying time | |||
| — | 4.0 | hr | |
| Hot air dryer | 2.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Barrel rear temperature | 260 | °C | |
| Barrel middle temperature | 260 to 270 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 290 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Injection pressure | 196 | MPa | |
| Back pressure | 1.96 to 3.92 | MPa | |
| Screw speed | 200 to 500 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.11 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |