| About |
|---|
| INFUSE™ 9000 Olefin Block Copolymer is a high performance olefin block copolymer that can be widely used in thermoplastic elastomer applications where higher service temperature requirements are needed. INFUSE 9000 also provides high filler loading capability along with low compression set and good processability. Main Characteristics: High upper service temperature performance Highly flexible with good elastic recovery Fast set up times for processability General purpose elastomer Excellent for compounds and blends Complies with EU, No 10/2011 U.S. FDA FCN 424 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | OBC |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.877 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.50 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, molded | 6.28 | MPa | ASTM D638 |
| fracture | 15.0 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, molded | 370 | % | ASTM D638 |
| fracture | 1200 | % | ASTM D412 |
| tear strength | 42.0 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395 | ||
| 23℃ | 23 | % | ASTM D395 |
| 70℃ | 45 | % | ASTM D395 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 120 | ℃ | Internal Method |
| TMA（1.00 mm） | 104 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw A, molded | 71 | ASTM D2240 | |
| Tensile modulus | |||
| 100% cut, molded | 3.29 | MPa | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1N, 5°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |