INFUSE™ 9077 is a high performance olefin block copolymer that can be compounded with a variety of polyolefins to make a thermoplastic elastomer suitable for XL foams and other applications This product is delivered with a nominal talc partitioning agent to assist in material handling. Main Characteristics Highly flexible Crosslinkable for foam applications Applications Compounding to make soft XL foams&& |
Product Description | |
---|---|
Supplier | DOW |
Generic | OBC |
Material Status | Commercial: Active |
Availabilitys | North America,Latin America,Asia Pacific,Europe |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 0.869 | g/cm³ | ASTM D792 |
Melt Flow Rate | |||
190℃,2.16kg | 0.50 | g/10min | ASTM D1238 |
elastic body | Nominal value | Unit | Test method |
---|---|---|---|
tear strength | 26.3 | kN/m | ASTM D624 |
Compression deformation | ASTM D395 | ||
23℃ | 20 | % | |
70℃ | 43 | % |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Glass transition temperature | -65.0 | ℃ | Internal Method |
Melting temperature | |||
DSC | 118 | ℃ | Internal Method |
TMA | 108 | ℃ | Internal Method |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Shore hardness | |||
Shaw A, molded | 51 | ASTM D2240 | |
Tensile modulus | |||
100% cut, molded | 1.21 | MPa | ASTM D638 |
tensile strength | |||
Fracture, molded | 3.00 | MPa | ASTM D638 |
Tensile strain | |||
Fracture, molded | > 1000 | % | ASTM D638 |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. Die C |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |