| Ingeo biopolymer 6201D, a NatureWorks LLC product, is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6201D is designed for extrusion into mechanically drawn staple fibers or continuous filament, using conventional fiber spinning and drawing equipment. 6201D is typically well suited for fiber processes where lower fiber shrinkage is desired: partially orientated yarn (POY), fully drawn yarn (FDY), staple fibers, and continuous filament. Ingeo biopolymer 6201D can be converted into a broad range of fiber products. Potential applications for PLA polymer 6201D include: Woven and knitted 100% continuous filament apparel Woven and knitted, intimate Staple blend fabrics including blends with cotton, wool, and other fibers Woven and knitted fabrics and netting for civil engineering applications Home furnishings&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources,Low contractility,Biodegradable,Food contact compliance,Compostable |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Modulus of Elasticity | 30.0 to 40.0 | g/denier | ASTM D2256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 55.0 to 60.0 | ℃ | ASTM D3417 |
| Crystallization peak temperature | |||
| DSC | 155 to 170 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Denier（per filament） | > 0.500 | ||
| Elongation of Fibers | 10 to 70 | % | ASTM D2256 |
| Tenacity of Fibers | 2.50 to 5.00 | g/denier | ASTM D2256 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 210℃，2.16kg | 15 to 30 | g/10min | ASTM D1238 |
| Relative viscosity | 3.10 | Internal Method | |
| Shrinkage rate | ASTM D2102 | ||
| boiled water | 5.0-15 | % | ASTM D2102 |
| Hot air: 130 ℃, 10 minutes | 5.0-15 | % | ASTM D2102 |
| Melt density | |||
| 230℃ | 1.08 | g/cm³ |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | < 5.0E-3 | % | |
| Melt temperature | 220 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10 min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |