INLUBE PCABSTF15

About
15% PTFE LUBRICATED POLYCARBONATE/ABS ALLOY&&

Product Description
Generic	PC+ABS
Material Status	Commercial: Active
Features	Lubricating
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.20	g/cm³	ASTM D792
Shrinkage rate
MD：3.2 mm	0.50 to 0.70	%

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	46.2	MPa	ASTM D638
Tensile strain
yield	10 to 20	%	ASTM D638
Bending modulus	2280	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
3.2mm	190	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	132	℃	ASTM D648

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	> 1.0E+17	ohms·cm	ASTM D257

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	93	°C
Drying time	3.0 to 4.0	hr
Recommended maximum moisture content	0.020	%
Processing (melt) temperature	246 to 271	°C
Mold temperature	60 to 82	°C
Back pressure	0.345 to 0.689	MPa
Screw speed	40 to 70	rpm
Vent depth	0.025 to 0.051	mm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.