| About |
|---|
| INNOMID ® CS 6-9830 is a 30 % glass-fibre-filled polyamide (PA-6) compound. This grade is available in nature and custom coloured form. Recommended application INNOMID ® CS 6-9830 is recommended for producing injection moulded products, where the required properties are high strength and stiffness.&& |
| Product Description | |
|---|---|
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Good Rigidity,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 46.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.70 | % | ISO 294-4 |
| MD | 0.10 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9400 | MPa | ISO 527-2/2 |
| tensile strength | |||
| fracture | 150 | MPa | ISO 527-2/1A/50 |
| Bending modulus | 6600 | MPa | ISO 178 |
| bending strength | 245 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 9.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 69 | kJ/m² | ISO 179/1eU |
| 23℃ | 73 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 9.0 | kJ/m² | ISO 180-A |
| 23℃ | 11 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | DIN 53482 |
| Compared to the leakage tracing index | |||
| Solution A | 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 220 to 260 | °C | |
| Barrel middle temperature | 220 to 260 | °C | |
| Barrel front temperature | 220 to 260 | °C | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection speed | 中等 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |