| About |
|---|
| InnoPlus HD2208J and HD2308J are high density polyethylene injection molding grade. They are tailored with narrow molecular weight distribution (MWD) result for good impact strength. Furthermore, they are UV stabilizer added that give the excellent UV resistance for outdoor applications such as auto part and industrial product. Typical Application: Crates, Pallets, Garbage bins, Industrial tubes, Fruit baskets, Caps and Closures&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Food contact compliance,Weight distribution,High density |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.5 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 25% non-ionic surfactant, F50 | 6.00 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 49 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 2 |
| Melting peak temperature | 131 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 65 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 30.4 | MPa | |
| fracture | 21.6 | MPa | |
| Tensile strain | |||
| fracture | > 1000 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1080 | MPa | ASTM D747 |
| Bending modulus | 1180 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 170 to 200 | °C | |
| Barrel middle temperature | 170 to 200 | °C | |
| Barrel front temperature | 170 to 200 | °C | |
| Nozzle temperature | 185 to 205 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Complete Break |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |