| InnoPlus HD2408J is high density polyethylene grade specially designed for high UV resistant requirement. It also exhibits high impact strength and good weathering resistance, suitable for outdoor applications. Typical Application : Crate, Pallet, Garbage bin, outdoor applications.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Food contact compliance,High density |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.964 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.5 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 25% non-ionic surfactant, F50 | 2.00 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 29 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 3 |
| Melting peak temperature | 131 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 65 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 30.4 | MPa | ASTM D638 |
| fracture | 11.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 750 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1080 | MPa | ASTM D747 |
| Bending modulus | 1570 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 170 to 200 | °C | |
| Barrel middle temperature | 170 to 200 | °C | |
| Barrel front temperature | 170 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Complete Break |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |