| About |
|---|
| InnoPlus HD7000H is high density polyethylene which has outstanding mechanical strength, good weathering resistance and excellent product appearance. It is suitable to produce not only truck-bed liner from sheet extrusion and thermoforming process but also automotive fuel tanks from blow molding process. Typical Application: Truck-bed liner, Automotive fuel tank&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good surface appearance,Food contact compliance,High density |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.10 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 10 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 25% non-ionic surfactant, F50 | > 1000 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 460 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 3 |
| Melting peak temperature | 130 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Temperature of hot forming mold | 210 to 230 | ℃ | |
| Blowing molding temperature | 190 to 220 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 27.5 | MPa | ASTM D638 |
| fracture | 39.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 900 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 834 | MPa | ASTM D747 |
| Bending modulus | 1080 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Non Break |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |