InnoPlus LD2420D

About
InnoPlus LD2420D is produced by high pressure tubular process, a technology licensed by LyondellBasell. This grade offers easy processability, good balance of mechanical and optical properties. Film extruded from InnoPlus LD2420D has high tensile strength, elongation, good toughness and good tear strength. Typical Applications : InnoPlus LD2420D is recommended for producing the heavy duty films, agricultural films, shrink films, tubes and small extrusion blow molding containers.&&

About

InnoPlus LD2420D is produced by high pressure tubular process, a technology licensed by LyondellBasell. This grade offers easy processability, good balance of mechanical and optical properties. Film extruded from InnoPlus LD2420D has high tensile strength, elongation, good toughness and good tear strength. Typical Applications : InnoPlus LD2420D is recommended for producing the heavy duty films, agricultural films, shrink films, tubes and small extrusion blow molding containers.&&

Product Description
Generic	LDPE
Material Status	Commercial: Active
Features	Excellent Processability,Good flexibility,Good Tensile Strength,Low density,Good tear strength
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.922	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	0.27	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
Compression Molding	240	MPa	ISO 527-2

film	Nominal value	Unit	Test method
film thickness
test	70	µm
tensile strength			ISO 527-3
Yield, molding	10.0	MPa	ISO 527-2
MD, fracture, 70 µ m, blow molded film	24.0	MPa
TD, fracture, 70 µ m, blow molded film	18.0	MPa
Tensile strain			ISO 527-3
MD, fracture, 70 µ m, blow molded film	320	%
TD, fracture, 70 µ m, blow molded film	550	%
Drop hammer impact
70 µ m, blow molded film	200	g	ASTM D1709

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	95.0	℃	ASTM D1525
Melting temperature	111	℃	ISO 11357-3

optical performance	Nominal value	Unit	Test method
gloss
20 °, 70 µ m, blow molded film	> 20		ASTM D2457
Haze
70.0 µ m, blow molded film	< 15	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	170 to 220	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.