InnoPlus LL7410D

About
InnoPlus LL7410D resin is a linear low density polyethylene with butene comonomers, with high content of slip and antiblock. This grade offers the excellent machinability on conversion lines. Films extruded from InnoPlus LL7410D have high tensile strength, elongation, good toughness and outstanding puncture strength. It is available for tubular blown film processing. Typical Applications : InnoPlus LL7410D is recommended for producing general purpose films, liners, food packaging, heavy duty and agricultural films.&&

About

InnoPlus LL7410D resin is a linear low density polyethylene with butene comonomers, with high content of slip and antiblock. This grade offers the excellent machinability on conversion lines. Films extruded from InnoPlus LL7410D have high tensile strength, elongation, good toughness and outstanding puncture strength. It is available for tubular blown film processing. Typical Applications : InnoPlus LL7410D is recommended for producing general purpose films, liners, food packaging, heavy duty and agricultural films.&&

Product Description
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Good flexibility,Smoothness,High anti-blocking,Machinable,Good Tensile Strength,Low density,Butylene copolymer,Puncture Resistant
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.921	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	25	µm
Secant modulus
1% secant, MD: 25 µ m, blow molded film	190	MPa
1% secant, TD: 25 µ m, blow molded film	230	MPa
tensile strength
MD, fracture, 25 µ m, blow molded film	34.0	MPa
TD, fracture, 25 µ m, blow molded film	26.0	MPa
Tensile strain
MD, fracture, 25 µ m, blow molded film	600	%
TD, fracture, 25 µ m, blow molded film	800	%
Drop hammer impact
25 µ m, blow molded film	100	g	ASTM D1709
Elmandorf tear strength
MD: 25 µ m, blow molded film	100	g
TD: 25 µ m, blow molded film	300	g

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	100	℃	ASTM D1525
Melting peak temperature	121	℃	ASTM D3418

optical performance	Nominal value	Unit	Test method
gloss
45 °, 25 µ m, blow molded film	50		ASTM D2457
Haze
25 µ m, blow molded film	17	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	160 to 180	°C
Nozzle temperature	170 to 190	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.