| About |
|---|
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good flexibility,Smoothness,High anti-blocking,Machinable,Good Tensile Strength,Low density,Butylene copolymer,Puncture Resistant |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.8 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| MD, 1% secant | 200 | MPa | ASTM D882 |
| TD, 1% secant | 200 | MPa | ASTM D882 |
| tensile strength | |||
| MD, fracture, 25 µ m, blow molded film | 30 | MPa | ASTM D882 |
| TD, fracture, 25 µ m, blow molded film | 23 | MPa | ASTM D882 |
| Tensile strain | |||
| MD, fracture, 25 µ m, blow molded film | 600 | % | ASTM D882 |
| TD, fracture, 25 µ m, blow molded film | 800 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 90 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD: 25 µ m, blow molded film | 100 | g | ASTM D1922 |
| TD: 25 µ m, blow molded film | 300 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 95 | ℃ | ASTM D1525 |
| Melting peak temperature | 121 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 45 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 15 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |