| InnoPlus LL9640U/LL9640UP are hexene co-polymer based linear low density polyethylene designed for rotational molding applications. These are UV8 resistance level rotational molding grades which provide an excellent impact strength and good end use performance with optimizing the balance between stiffness and environmental stress cracking resistance. InnoPlus LL9640UP is a powder form of InnoPlus LL9640U. Typical Applications : InnoPlus LL9640U/LL9640UP can be used to produce variety applications such as general molding, toys & playground equipment, outdoor storage containers, medium to large water tanks and chemical tanks.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Low density,Copolymer,Hexene copolymers |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.932 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, molded, F50 | > 1000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| Compression Molding | 240 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 110 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 56 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| Yield, molding | 15.0 | MPa | ASTM D638 |
| Fracture, molded | 25.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 1000 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 550 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Partial Break |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |