| About |
|---|
| INNOPOL CS 1-3130 MA is a 30 % talcum filled compound based on polypropylene homopolymer. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 1-3130 MA is recommended especially for producing products, where high stiffness, low shrinkage and long term heat stability required.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Low contractility,Heat Stabilized,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 32.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.6 | % | ISO 527-2/50 |
| Bending modulus | 3600 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 2.1 | kJ/m² | ISO 179/1eA |
| 23℃ | 2.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 14 | kJ/m² | ISO 179/1eU |
| 23℃ | 27 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 123 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 67.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 153 | ℃ | ISO 306/A120 |
| B120 | 92.0 | ℃ | ISO 306/B120 |
| Melting temperature | 164 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Automotive materials, thickness d>1 mm | + | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Barrel rear temperature | 190 to 250 | °C | |
| Barrel middle temperature | 190 to 250 | °C | |
| Barrel front temperature | 190 to 250 | °C | |
| Processing (melt) temperature | 210 to 260 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |