| About |
|---|
| INNOPOL ® CS 1-7830 HGF is a 30 % glass-fibre-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 1-7830 HGF is recommended to be used for applications where the required properties are high strength and stiffness besides long term heat stability.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Heat Stabilized,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，5.0kg | 6.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 6500 | MPa | ISO 527-2/2 |
| tensile strength | |||
| Yield, injection molding | 90.0 | MPa | |
| Fracture, injection molding | 87.0 | MPa | |
| Tensile strain | |||
| Yield, injection molding | 2.8 | % | |
| Fracture, injection molding | 4.5 | % | |
| Bending modulus | |||
| injection molding | 6000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30 ℃, injection molding | 7.0 | kJ/m² | |
| 23 ℃, injection molding | 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30 ℃, injection molding | 50 | kJ/m² | |
| 23 ℃, injection molding | 53 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 157 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 140 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 163 | ℃ | ISO 306/A120 |
| B120 | 134 | ℃ | ISO 306/B120 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Barrel rear temperature | 190 to 240 | °C | |
| Barrel middle temperature | 190 to 240 | °C | |
| Barrel front temperature | 190 to 240 | °C | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 15 to 50 | °C | |
| Injection speed | 中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |