| About |
|---|
| INNOPOL ® CS 2-8000 is a polypropylene block-copolymer. This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 2-8000 is highly suitable for pipe manufacturing where the required property is high impact resistance besides good stiffness.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,High impact resistance,Block Copolymer |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.40 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 28.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 5.2 | kJ/m² | ISO 179/1eA |
| 23℃ | 65 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 87.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 48.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 150 | ℃ | ISO 306/A120 |
| B120 | 79.0 | ℃ | ISO 306/B120 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.50 | % | |
| Barrel rear temperature | 190 to 260 | °C | |
| Barrel middle temperature | 190 to 260 | °C | |
| Barrel front temperature | 190 to 260 | °C | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 15 to 50 | °C | |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel 1 zone temperature | 180 to 220 | °C | |
| Barrel 2 zone temperature | 180 to 220 | °C | |
| Barrel 3 zone temperature | 180 to 220 | °C | |
| Barrel 4 zone temperature | 180 to 220 | °C | |
| Barrel 5 zone temperature | 180 to 220 | °C | |
| Melt temperature | 200 to 230 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |