| About |
|---|
| Innoprene 1350N/B is a Thermoplastic Vulcanizate (TPV) material. It is available in Asia Pacific, Europe, Latin America, or North America for blow molding, calendering, extrusion, or injection molding. Important attributes of Innoprene 1350N/B are: Chemical Resistant Eco-Friendly/Green Fatigue Resistant Good Flexibility Good Tear Strength Typical applications include: Appliances Automotive Business/Office Goods Construction Applications Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Good Dimensional Stability,Good Electrical Properties,Renewable resources,High Heat Resistance,Fatigue resistance,Good tear strength,Ozone resistance,Solvent resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D792 |
| 25℃ | 0.948 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 25 ℃ | 4.41 | MPa | ISO 37 |
| Yield, 25 ℃ | 4.41 | MPa | ASTM D412 |
| 100% strain, 25 ℃ | 0.981 | MPa | ASTM D412 |
| 100% strain, 25 ℃ | 0.981 | MPa | ISO 37 |
| Tensile strain | |||
| Fracture, 25 ℃ | 670 | % | ISO 37 |
| Fracture, 25 ℃ | 670 | % | ASTM D412 |
| tear strength | |||
| 25℃ | 19.6 | kN/m | ASTM D624 |
| 25℃ | 20 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395 | ||
| 120℃，70 hr | 38 | % | ISO 815 |
| 70℃，22 hr | 30 | % | ASTM D395 |
| 120℃，70 hr | 38 | % | ASTM D395 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 25 ℃ | 38 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Brittleness Temperature（Type B） | -62.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 150℃，168 hr | -6.0 | % | ISO 188 |
| 150℃，168 hr | -6.0 | % | ASTM D412 |
| The rate of change in ultimate elongation in air | |||
| 150℃，168 hr | -10 | % | ASTM D412 |
| Change in Tensile Strain at Break in Air（150℃，168 hr） | -10 | % | ISO 188 |
| The rate of change of Shore hardness in air | |||
| Shaw A, 150 ℃, 168 hr | 1.0 | ISO 188 | |
| Quality change rate | ASTM D471 | ||
| 25℃，168 hr，in Hydrochloric Acid，10% | 4.0 | % | ASTM D471 |
| 25℃，168 hr，in Sodium Hydroxide，50% | 1.0 | % | ASTM D471 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| UV Resistance（1000hr） | <1.0 E | SAE J1960 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 85 | °C | |
| Drying time | 3.0 | hr | |
| Barrel rear temperature | 160 to 180 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 200 | °C | |
| Nozzle temperature | 200 to 220 | °C | |
| Processing (melt) temperature | 190 to 230 | °C | |
| Mold temperature | 10 to 60 | °C | |
| Injection speed | Fast | ||
| Drying temperature | 85 | °C | |
| Drying time | 3.0 | hr | |
| Hopper temperature | 160 to 170 | °C | |
| Barrel 1 zone temperature | 180 to 200 | °C | |
| Barrel 2 zone temperature | 180 to 200 | °C | |
| Barrel 3 zone temperature | 180 to 200 | °C | |
| Connector temperature | 200 | °C | |
| Melt temperature | 190 to 230 | °C | |
| Nozzle temperature | 180 to 210 | °C | |
| Back pressure | 5.00 to 20.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |