| About |
|---|
| Characteristics: Average flow Excellent processability Process: Injection, extrusion and thermoforming Coextrusion (gloss layer) Applications: Disposables Packagings Household wares School articles&& |
| Product Description | |
|---|---|
| Generic | PS (GPPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Food contact compliance,Disposable |
| Availabilitys | Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 5.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.30 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2960 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 51.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 23℃ | 3100 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 97.0 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 98.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 4 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.90 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 210 to 260 | °C | |
| Mold temperature | 50 to 75 | °C | |
| Melt temperature | 210 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 120°C/h |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |