| About |
|---|
| INSPIRE™ 227 高性能聚合物综合了良好的加工性能和优异的挺度以及较低的晶点含量，用于高质量薄膜的挤出加工。 主要特性： 优异的挺度 耐高温性能 晶点含量低 加工性能好 光学性能好 符合以下法规： EU, No 10/2011 请查询法规以获取完备的细节资料。&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.2 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Membrane puncture strength | |||
| 50 µm | 0.500 | J | ASTM D5748 |
| Membrane puncture force | |||
| 50 µm | 42.0 | N | ASTM D5748 |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 50 µ m | 1170 | MPa | |
| 2% secant, TD: 50 µ m | 1140 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m | 27.0 | MPa | |
| TD, yield, 50 µ m | 41.0 | MPa | |
| MD, fracture, 50 µ m | 38.0 | MPa | |
| TD, fracture, 50 µ m | 39.0 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 50 µ m | 250 | % | |
| TD, fracture, 50 µ m | 6.0 | % | |
| Drop hammer impact | |||
| 50 µm | 50 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：50 µm | 14 | g | |
| TD：50 µm | 24 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 162 to 166 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，50 µm | 32 | ASTM D2457 | |
| Haze | |||
| 50 µm | 23 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |