| INSPIRE™ 361 高性能聚合物时专为薄膜挤出加工而研发的。INSPIRE™ 361 高性能聚合物具有透明度高的特点。 INSPIRE 361 高性能聚合物的应用领域： 薄膜 收缩膜 法规信息 INSPIRE™ 361 高性能聚合物应该符合以下法规的要求： 欧盟指令2002/72/EC 美国食品和药物管理局法规 21 CFR 177.1520(c) 3.1a 请查询适用的法规以获取完备的细节资料&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 50 µ m, blow molded film | 810 | MPa | |
| 1% secant, TD, 50 µ m, blow molded film | 790 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 47.0 | MPa | |
| TD, fracture, 50 µ m, blow molded film | 32.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 580 | % | |
| TD, fracture, 50 µ m, blow molded film | 500 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 129 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 80 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 3.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |