| About |
|---|
| INZEA injection grades are biobased polymers with a renewable content from 40 to 85% and they can be processed in conventional equipment for polyolefins or PS. INZEA delivers similar properties to common plastics. Its use is focused on applications with a shorter lifespan, or ones which are difficult to collect once used and even in promotional gifts. Disposable catering articles such as trays, bowls, plates, cups and cutlery, coffee capsules, or various products used in agriculture, such as clips or seed pots, are safe bets for a change. Also various office products such as paper clips, pens and pencils, little containers or pins.&& |
| Product Description | |
|---|---|
| Generic | 生物可降解聚合物 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable,Food contact compliance,Compostable |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 8.1 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 8.00 | cm³/10min | ISO 1133 |
| water content | < 1.0 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2860 | MPa | ISO 527-1-2 |
| tensile strength | |||
| 23℃ | 52.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.5 | % | |
| Fracture, 23 ℃ | 8.0 | % | |
| Bending modulus | |||
| 23℃ | 2800 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 42.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² | ISO 179/1e |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 52.0 to 56.0 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 140 to 155 | ℃ | ISO 3146 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Renewable Content | 85 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |