| About |
|---|
| IPETHENE® 210 is a low density polyethylene extrusion grade, produced by high pressure autoclave technology. It is designed for thin film applications with good optical and processing properties. Additives This grade does not contain additives. Applications IPETHENE® 210 is suitable for carrier and shopping bags, liners, pouches, general packaging and thin shrink films.&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Optical performance,Low density |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 27.0 | MPa | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 24.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 450 | % | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 700 | % | ISO 527-3 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 200 | g | ISO 7765-1/A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 50 µ m, blow molded film | 3.9 | N | ISO 6383-2 |
| TD: 50 µ m, blow molded film | 2.5 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 94.0 | ℃ | ISO 306 |
| Melting temperature | 109 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 66 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 7.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. By DSC |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |