| About |
|---|
| IROGRAN A 78 E 4506 is a thermoplastic polyester-polyurethane for injection moulding and extrusion applications. Additional characteristics of the product are excellent mechanical properties and high tear strength. PERFORMANCE FEATURES High production rates Good melt flow Softener-free High oil resistance Dynamically highly loadable APPLICATIONS For the production of profiles, spiral hoseshoses, jackets for high pressure hoses.&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Good liquidity,Good tear strength,Grease resistance |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | |
| Melt Volume Rate | |||
| 190℃，21.6 kg | 25.0 | cm³/10min | |
| Shrinkage rate | |||
| MD: Injection molding | 0.90 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, injection molding | 80 | ASTM D2240 | |
| Shaw’s D, injection molding | 30 | ASTM D2240 | |
| Shore hardness | ISO 868 | ||
| Shaw A, injection molding | 80 | ISO 868 | |
| Shaw’s D, injection molding | 30 | ISO 868 | |
| Abrasion | 25 | mm³ | ISO 4649 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 50.0 | MPa | DIN 53504 |
| 300% strain | 8.00 | MPa | DIN 53504 |
| 100% strain | 4.40 | MPa | DIN 53504 |
| Tensile strain | |||
| fracture | 700 | % | DIN 53504 |
| tear strength | 60 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395 | ||
| 23℃，24 hr | 25 | % | ASTM D395 |
| 70℃，24 hr | 40 | % | ASTM D395 |
| Compression deformation | ISO 815 | ||
| 23℃，24 hr | 25 | % | ISO 815 |
| 70℃，24 hr | 40 | % | ISO 815 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 100 to 110 | °C | |
| Hot Air Dryer | 80 to 90 | °C | |
| Drying time | |||
| — | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Barrel rear temperature | 175 to 195 | °C | |
| Barrel middle temperature | 175 to 195 | °C | |
| Barrel front temperature | 175 to 195 | °C | |
| Nozzle temperature | 180 to 200 | °C | |
| Processing (melt) temperature | 170 to 190 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 | hr | |
| Hopper temperature | 25 to 40 | °C | |
| Barrel 1 zone temperature | 165 to 190 | °C | |
| Barrel 2 zone temperature | 165 to 190 | °C | |
| Barrel 3 zone temperature | 165 to 190 | °C | |
| Barrel 4 zone temperature | 165 to 190 | °C | |
| Barrel 5 zone temperature | 165 to 190 | °C | |
| Connector temperature | 175 to 195 | °C | |
| Nozzle temperature | 175 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |