| About |
|---|
| IROGRAN A 78 P 4766 is a flame-retardant, halogen-free, thermoplastic polyether-polyurethane intended for extrusion and injection moulding applications. Additional characteristics of the product is the high flexibility and elasticity. PERFORMANCE FEATURES High hydrolysis resistance High microbial resistance Flame retardant Halogen-free UL 94 classification V0 APPLICATIONS Cables Hoses Spiral Hoses Profiles Cable Bushings&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Good flexibility,High elastic,Hydrolysis stability,Antimicrobial properties,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，21.6 kg | 110 | cm³/10min | |
| Shrinkage rate | |||
| MD: Injection molding | 1.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw A, injection molding | 82 | ISO 868 | |
| Shaw’s D, injection molding | 30 | ISO 868 | |
| Shore hardness | ASTM D2240 | ||
| Shaw A, injection molding | 82 | ASTM D2240 | |
| Shaw’s D, injection molding | 30 | ASTM D2240 | |
| Abrasion | 40 | mm³ | ISO 4649 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 30.0 | MPa | DIN 53504 |
| fracture | 27.6 | MPa | ASTM D412 |
| 300% strain | 8.00 | MPa | DIN 53504 |
| 300% strain | 9.65 | MPa | ASTM D412 |
| 100% strain | 5.20 | MPa | DIN 53504 |
| 100% strain | 5.79 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 800 | % | ASTM D412 |
| fracture | 800 | % | DIN 53504 |
| tear strength | 71.8 | kN/m | ASTM D624 |
| tear strength | 40 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395 | ||
| 23℃，24 hr | 20 | % | ASTM D395 |
| 70℃，24 hr | 40 | % | ASTM D395 |
| Compression deformation | ISO 815 | ||
| 23℃，24 hr | 20 | % | ISO 815 |
| 70℃，24 hr | 40 | % | ISO 815 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| TMA | Internal Method | ||
| High：635.0 µm | 190 | ℃ | Internal Method |
| Low：635.0 µm | 165 | ℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 100 to 110 | °C | |
| Hot Air Dryer | 80 to 90 | °C | |
| Drying time | |||
| — | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30 | °C | |
| Barrel rear temperature | 175 to 195 | °C | |
| Barrel middle temperature | 175 to 195 | °C | |
| Barrel front temperature | 175 to 195 | °C | |
| Nozzle temperature | 180 to 200 | °C | |
| Processing (melt) temperature | 170 to 195 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 | hr | |
| Hopper temperature | 25 to 40 | °C | |
| Barrel 1 zone temperature | 165 to 190 | °C | |
| Barrel 2 zone temperature | 165 to 190 | °C | |
| Barrel 3 zone temperature | 165 to 190 | °C | |
| Barrel 4 zone temperature | 165 to 190 | °C | |
| Barrel 5 zone temperature | 165 to 190 | °C | |
| Connector temperature | 175 to 195 | °C | |
| Nozzle temperature | 175 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 3. Extruded Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |