| About |
|---|
| IROGRAN A 85 D 5001 DP is a antistatic, polyester based thermoplastic polyurethane intended for extrusion applications and injection moulding. IROGRAN A 85 D 5001 DP is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable in flat die, cast die extrusion processes. IROGRAN A 85 D 5001 DP is a development material. PERFORMANCE FEATURES Excellent wear performance Good processability Antistatic behaviour Good melt flow High elasticity&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Good flexibility,High elastic,Hydrolysis stability,Good liquidity,Good wear resistance,Antistatic property |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Density | 1.19 | g/cm³ | DIN 53479 |
| Melt Volume Rate | |||
| 190℃，21.6 kg | 75.0 | cm³/10min | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, injection molding | 85 | ASTM D2240 | |
| Shaw’s D, injection molding | 34 | ASTM D2240 | |
| Shore hardness | DIN 53505 | ||
| Shaw A, injection molding | 85 | DIN 53505 | |
| Shaw’s D, injection molding | 34 | DIN 53505 | |
| Wear amount | |||
| — | 25 | mm³ | DIN 53516 |
| — | 25 | mm³ | ASTM D395 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 40.0 | MPa | DIN 53504 |
| fracture | 40.0 | MPa | ASTM D412 |
| 300% strain | 11.0 | MPa | DIN 53504 |
| 300% strain | 5.58 | MPa | ASTM D412 |
| 100% strain | 5.58 | MPa | ASTM D412 |
| 100% strain | 5.00 | MPa | DIN 53504 |
| Tensile strain | |||
| fracture | 620 | % | DIN 53504 |
| fracture | 830 | % | ASTM D412 |
| tear strength | 105 | kN/m | ASTM D624 |
| tear strength | 70 | kN/m | ISO 34-1 |
| Basho’s elasticity | 36 | % | ASTM D2632 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+8 | ohms |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 100 to 110 | °C | |
| Hot Air Dryer | 80 to 90 | °C | |
| Drying time | |||
| — | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30 | °C | |
| Hopper temperature | 25 to 45 | °C | |
| Barrel rear temperature | 190 to 210 | °C | |
| Barrel middle temperature | 190 to 210 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 185 to 210 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 | hr | |
| Hopper temperature | 25 to 40 | °C | |
| Barrel 1 zone temperature | 180 to 205 | °C | |
| Barrel 2 zone temperature | 180 to 205 | °C | |
| Barrel 3 zone temperature | 180 to 205 | °C | |
| Barrel 4 zone temperature | 180 to 205 | °C | |
| Barrel 5 zone temperature | 180 to 205 | °C | |
| Connector temperature | 180 to 205 | °C | |
| Nozzle temperature | 185 to 205 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |