| About |
|---|
| IROGRAN A 85 P 4394 is a high performance polyether based thermoplastic polyurethane intended for extrusion and injection moulding applications. IROGRAN A 85 P 4394 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of tubing, cable jacketing and technical mouldings. PERFORMANCE FEATURES High tensile strength Excellent wear performance Excellent hydrolysis & microbial resistance Good low temperature flexibility&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Hydrolysis stability,Antimicrobial properties,Good Tensile Strength,Low temperature toughness,Good wear resistance |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，21.6 kg | 55.0 | cm³/10min | |
| Shrinkage rate | |||
| MD: Injection molding | 0.80 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, injection molding | 85 | ASTM D2240 | |
| Shaw’s D, injection molding | 36 | ASTM D2240 | |
| Shore hardness | ISO 868 | ||
| Shaw A, injection molding | 85 | ISO 868 | |
| Shaw’s D, injection molding | 36 | ISO 868 | |
| Abrasion | 25 | mm³ | ISO 4649 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 45.0 | MPa | DIN 53504 |
| fracture | 35.0 | MPa | ASTM D412 |
| 300% strain | 12.0 | MPa | ASTM D412 |
| 300% strain | 12.0 | MPa | DIN 53504 |
| 100% strain | 7.00 | MPa | DIN 53504 |
| 100% strain | 7.00 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 610 | % | ASTM D412 |
| fracture | 640 | % | DIN 53504 |
| tear strength | 101 | kN/m | ASTM D624 |
| tear strength | 60 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395 | ||
| 23℃，24 hr | 20 | % | ASTM D395 |
| 70℃，24 hr | 40 | % | ASTM D395 |
| Compression deformation | ISO 815 | ||
| 23℃，24 hr | 20 | % | ISO 815 |
| 70℃，24 hr | 40 | % | ISO 815 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| TMA | Internal Method | ||
| High：635.0 µm | 170 | ℃ | Internal Method |
| Low：635.0 µm | 150 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 100 to 110 | °C | |
| Hot Air Dryer | 80 to 90 | °C | |
| Drying time | |||
| — | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30 | °C | |
| Barrel rear temperature | 175 to 210 | °C | |
| Barrel middle temperature | 175 to 210 | °C | |
| Barrel front temperature | 175 to 210 | °C | |
| Nozzle temperature | 200 to 210 | °C | |
| Processing (melt) temperature | 190 to 205 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 | hr | |
| Hopper temperature | 25 to 40 | °C | |
| Barrel 1 zone temperature | 160 to 200 | °C | |
| Barrel 2 zone temperature | 160 to 200 | °C | |
| Barrel 3 zone temperature | 160 to 200 | °C | |
| Barrel 4 zone temperature | 160 to 200 | °C | |
| Barrel 5 zone temperature | 160 to 200 | °C | |
| Connector temperature | 175 to 200 | °C | |
| Nozzle temperature | 175 to 205 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 3. Extruded Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |