| IROGRAN A 85 P 4854 is a flame-retardant, halogen-free polyether based thermoplastic polyurethane intended for extrusion and injection moulding applications. IROGRAN A 85 P 4854 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of cable jacketing where enhanced fire retardency is required. PERFORMANCE FEATURES High tensile strength Excellent wear performance Excellent hydrolysis & microbial resistance Good low temperature flexibility Halogen free Flame retardant Matt surface UL 94 Classification V0&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Hydrolysis stability,Antimicrobial properties,Halogen free,Flame Characteristics,Good Tensile Strength,Low temperature toughness,Good wear resistance,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，21.6 kg | 150 | cm³/10min | |
| Shrinkage rate | |||
| MD: Injection molding | 0.80 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw A, injection molding | 83 | ISO 868 | |
| Shaw’s D, injection molding | 33 | ISO 868 | |
| Shore hardness | ASTM D2240 | ||
| Shaw A, injection molding | 83 | ASTM D2240 | |
| Shaw’s D, injection molding | 33 | ASTM D2240 | |
| Abrasion | 40 | mm³ | ISO 4649 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 25.0 | MPa | DIN 53504 |
| fracture | 25.0 | MPa | ASTM D412 |
| 300% strain | 7.50 | MPa | ASTM D412 |
| 300% strain | 7.50 | MPa | DIN 53504 |
| 100% strain | 3.50 | MPa | DIN 53504 |
| 100% strain | 3.50 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 670 | % | DIN 53504 |
| fracture | 670 | % | ASTM D412 |
| tear strength | 35.0 | kN/m | ASTM D624 |
| tear strength | 35 | kN/m | ISO 34-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| TMA | Internal Method | ||
| High：635.0 µm | 180 | ℃ | Internal Method |
| Low：635.0 µm | 125 | ℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 80 to 90 | °C | |
| Hot Air Dryer | 60 to 70 | °C | |
| Drying time | |||
| — | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30 | °C | |
| Barrel rear temperature | 170 to 210 | °C | |
| Barrel middle temperature | 170 to 210 | °C | |
| Barrel front temperature | 170 to 210 | °C | |
| Nozzle temperature | 200 to 210 | °C | |
| Processing (melt) temperature | 190 to 205 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 | hr | |
| Hopper temperature | 25 to 40 | °C | |
| Barrel 1 zone temperature | 160 to 200 | °C | |
| Barrel 2 zone temperature | 160 to 200 | °C | |
| Barrel 3 zone temperature | 160 to 200 | °C | |
| Barrel 4 zone temperature | 160 to 200 | °C | |
| Barrel 5 zone temperature | 160 to 200 | °C | |
| Connector temperature | 175 to 200 | °C | |
| Nozzle temperature | 175 to 205 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 3. Extruded Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |