| IROGRAN A 92 E 5670 FCM is a thermoplastic polyester polyurethane for melt calendering. IROGRAN is part of the HUNTSMAN technical extrusion/injection molding product range and offers a specially designed, flexible material with a broad processing window. IROGRAN A 92 E 5670 FCM is a food contact material. PERFORMANCE FEATURES High oil resistance High production rate Good melt flow Easy coloring Complies with FDA CFR 175.105 / 177.2600 APPLICATION Cable jacketing Tubing Technical extrusion&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good liquidity,Food contact compliance,Grease resistance,Good coloring |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | DIN 53479 |
| Melt Flow Rate | |||
| 190℃，10.0kg | 62 | g/10min | |
| Shrinkage rate | |||
| MD: Injection molding | 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | DIN 53505 | ||
| Shaw A, injection molding | 91 | DIN 53505 | |
| Shaw’s D, injection molding | 37 | DIN 53505 | |
| Shore hardness | ASTM D2240 | ||
| Shaw A, injection molding | 91 | ASTM D2240 | |
| Shaw’s D, injection molding | 37 | ASTM D2240 | |
| Wear amount | |||
| — | 20 | mm³ | DIN 53516 |
| — | 20 | mm³ |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 0.635 mm | 36.0 | MPa | DIN 53504 |
| Tensile strain | |||
| Fracture, 0.635 mm | 580 | % | DIN 53504 |
| tear strength | |||
| 0.635 mm | 83 | kN/m | DIN 53515 |
| Compression deformation | ASTM D395 | ||
| 23℃，24 hr | 25 | % | ASTM D395 |
| 70℃，24 hr | 40 | % | ASTM D395 |
| Compression deformation | DIN 53517 | ||
| 23℃，24 hr | 25 | % | DIN 53517 |
| 70℃，24 hr | 40 | % | DIN 53517 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| TMA | Internal Method | ||
| High | 170 | ℃ | Internal Method |
| Low | 124 | ℃ | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Calendar Temperature Profile | |||
| Front Roll（32rpm） | 170 to 190 | ℃ | |
| Rear Roll（27rpm） | 170 to 190 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 85 to 90 | °C | |
| Drying time | 3.0 | hr | |
| Hopper temperature | 25 to 40 | °C | |
| Barrel 1 zone temperature | 195 | °C | |
| Barrel 2 zone temperature | 195 | °C | |
| Barrel 3 zone temperature | 195 | °C | |
| Barrel 4 zone temperature | 195 | °C | |
| Barrel 5 zone temperature | 195 | °C | |
| Connector temperature | 210 | °C | |
| Nozzle temperature | 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 3. Extruded Film |
| 4. 2 Roll Mill |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |