ISPLEN® PB 130 G1F

About
ISPLEN® PB 130 G1F is a heterophasic copolymer with medium-low fluidity designed for extrusion applications. It has good processability and high mechanical properties especially high impact strength, even at low temperatures. ISPLEN® PB 130 G1F can be easily coloured during the extrusion process using the right pigments, preferably in the form of concentrates with a higher melt flow rate than the base polymer. TYPICAL APPLICATIONS In extrusion and blow-moulding processes, such as: Films and sheets with a good surface gloss Pipes Blow- moulding Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.&&

About

ISPLEN® PB 130 G1F is a heterophasic copolymer with medium-low fluidity designed for extrusion applications. It has good processability and high mechanical properties especially high impact strength, even at low temperatures. ISPLEN® PB 130 G1F can be easily coloured during the extrusion process using the right pigments, preferably in the form of concentrates with a higher melt flow rate than the base polymer. TYPICAL APPLICATIONS In extrusion and blow-moulding processes, such as: Films and sheets with a good surface gloss Pipes Blow- moulding Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.&&

Product Description
Supplier	REPSOL
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Excellent Processability,High impact resistance,Food contact compliance,Moderate liquidity,low-temperature impact resistance,Good coloring
Availabilitys	North America,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	1.3	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	60		ISO 868
tensile strength
yield	27.0	MPa	ISO 527-2
Bending modulus	1100	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	6.0	kJ/m²	ISO 179
23℃	30	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	74.0	℃	ISO 75-2/B
Vicat Softening Temp	150	℃	ISO 306/A

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	190 to 250	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.