| Polypropylene copolymer compound, with 20% mineral fillers reinforced and medium melt flow rate. ISPLEN® PM275 AW gives a good compromise between stiffness and impact strength, a low warpage and shrinkage behaviour. The product is high UV stabilised. APPLICATIONS Automotive: Interior trims and panels. Technical pieces, in general.&& |
| Product Description | |
|---|---|
| Supplier | REPSOL |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Low warping,High impact resistance,Low contractility,Moderate liquidity |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | 1.0 to 1.1 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 2300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20℃ | 4.0 | kJ/m² | ISO 179 |
| 0℃ | 5.0 | kJ/m² | ISO 179 |
| 23℃ | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -20℃ | 70 | kJ/m² | ISO 179 |
| 0℃ | 95 | kJ/m² | ISO 179 |
| 23℃ | 无断裂 | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 102 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 58.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 146 | ℃ | ISO 306/A120 |
| B120 | 71.0 | ℃ | ISO 306/B120 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x100x3mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |