| Iupilon® GSH2030R2 K807是一种聚碳酸酯（PC）材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Iupilon® GSH2030R2 K807的主要特性有: 阻燃/额定火焰 抗翘曲&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low warping,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 14.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.20 to 0.40 | % | |
| MD：3.2 mm | 0.20 to 0.40 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.090 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5100 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 51.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.9 | % | ISO 527-2 |
| Bending modulus | 4600 | MPa | ISO 178 |
| bending strength | 100 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 27 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 134 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 140 | ℃ | ISO 75-2/B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 270 to 290 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 290 to 310 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |