| About |
|---|
| Iupilon® GSH2050DF is a Polycarbonate (PC) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® GSH2050DF are: Flame Rated Warp Resistant&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low warping,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 2.2 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 1.70 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.10 to 0.30 | % | |
| MD：3.2 mm | 0.10 to 0.30 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.070 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11600 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 102 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.4 | % | ISO 527-2 |
| Bending modulus | 10800 | MPa | ISO 178 |
| bending strength | 160 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 31 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 138 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 144 | ℃ | ISO 75-2/B |
| Linear coefficient of thermal expansion | |||
| TD | 3.9E-5 | 1/℃ | ISO 11359-2 |
| MD | 1.8E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 270 to 290 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 290 to 310 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |