| Iupilon® S-2000F是一种粉状聚碳酸酯（PC）材料。 该产品在北美洲、欧洲或亚太地区有供货,加工方式为:挤出成型。 Iupilon® S-2000F的主要特性为中等粘度，典型应用领域为改性加工行业。一般的包装为650kg/包。常见产地有：三菱瓦斯化学工程塑料（上海）有限公司 |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High purity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | |
| MD：3.2 mm | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.24 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 61.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 5.6 | % | ISO 527-2 |
| Nominal tensile fracture strain | 110 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 93.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 76 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 143 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 129 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 6.5E-5 | 1/℃ | |
| TD | 6.6E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 6.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 1 mm | 31 | kV/mm | |
| 3 mm | 18 | kV/mm | |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 3.10 | ||
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 6.0E-4 | ||
| 1 MHz | 9.0E-3 | ||
| Compared to the leakage tracing index | PLC 2 | UL 746 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| drying temperature | 120 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Temperature at the rear of the barrel | 260 to 280 | °C | |
| Temperature in the middle of the barrel | 270 to 290 | °C | |
| Front temperature of material barrel | 270 to 300 | °C | |
| Nozzle temperature | 270 to 300 | °C | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |