| Ixef® 1002 is a 30% glass-fiber reinforced, general purpose polyarylamide compound which exhibits high strength and rigidity, outstanding surface finish, and excellent creep resistance. Black: Ixef® 1002/9008 Natural: Ixef® 1002/0008 Custom colorable&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,Good Dimensional Stability,High liquidity,Solvent resistance,Low moisture absorption,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.10 to 0.40 | % | Internal Method |
| Water absorption rate | |||
| Balance, 65% RH | 1.9 | % | Internal Method |
| 23℃，24hr | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 190 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | 11500 | MPa | ISO 178 |
| bending strength | 285 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 70 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 460 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 1.8E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 110 Hz | 3.90 | IEC 60250 | |
| Dissipation factor | |||
| 110 Hz | 0.010 | IEC 60250 | |
| Compared to the leakage tracing index | 400 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 | |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 0.50 to 1.5 | hr | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel front temperature | 260 to 290 | °C | |
| Processing (melt) temperature | 280 | °C | |
| Mold temperature | 120 to 140 | °C | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |