| About |
|---|
| Ixef® BM-1524 is a 50% glass-fiber reinforced, halogen-free flame retardant polyarylamide developed for aircraft cabin interior applications that require high strength and stiffness, good surface finish, low moisture absorption, and excellent chemical and creep resistance. This product is qualified under Boeing BMS8-270 Rev. L, Type I, Class 6, Form B, Grade 50 and meets the FAA 60-second vertical burn requirements per 14 CFR 25.853 Appendix F and toxic gas emission requirements per BSS7239 and ABD0031. Natural: Ixef® BM-1524 NT 000&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,Good Dimensional Stability,High liquidity,Halogen free,Flame Characteristics,Solvent resistance,Low moisture absorption,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.69 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| balance | 0.28 | % | ISO 62 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 20000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 248 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.3 | % | ASTM D638 |
| Bending modulus | 19300 | MPa | ASTM D790 |
| bending strength | |||
| yield | 376 | MPa | ASTM D790 |
| Compression modulus | 16500 | MPa | ASTM D695 |
| compressive strength | 328 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 227 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 2.40 GHz | 4.44 | ASTM D2520 | |
| Dissipation factor | |||
| 2.4 GHz | 0.012 | ASTM D2520 | |
| Compared to the resistance to leakage and marking index | |||
| 3.00 mm | > 600 | V | UL 746 |
| Compared to the leakage tracing index | > 600 | V | IEC 60112 |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.400 mm | 37.6 | UL 746 | |
| 0.750 mm | 53.6 | UL 746 | |
| 1.50 mm | 70.2 | UL 746 | |
| 3.00 mm | 95.4 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.40 mm | PLC 2 | UL 746 | |
| 0.75 mm | PLC 2 | UL 746 | |
| 1.5 mm | PLC 1 | UL 746 | |
| 3.0 mm | PLC 1 | UL 746 | |
| High voltage arc ignition resistance index (HVAR) (3.00 mm) | PLC 0 | UL 746 | |
| High voltage arc marking rate (HVTR) (3.00 mm) | PLC 0 | UL 746 | |
| 0.400 mm | 95 | sec | UL 746 |
| 0.750 mm | > 120 | sec | UL 746 |
| 1.50 mm | > 120 | sec | UL 746 |
| 3.00 mm | > 120 | sec | UL 746 |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| HWI | UL 746 | ||
| 0.40 mm | PLC 1 | UL 746 | |
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm, all colors | V-0 | UL 94 | |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.4 mm | 775 | ℃ | IEC 60695-2-13 |
| 0.75 mm | 800 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 825 | ℃ | IEC 60695-2-13 |
| 3 mm | 850 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 37 | % | ISO 4589-2 |
| Toxic gas emissions | BSS 7239/ATS 1000/ABD 0031 | ||
| CO | 100 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| HCL | < 1 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| HCN | 15 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| HF | < 1 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| NO + NO2 | < 1 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| SO2 | < 1 | ppm | BSS 7239/ATS 1000/ABD 0031 |
| Vertical combustion test | |||
| 60 second，8.89 cm | 5.0 | sec | DMS 1510 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 1.0 to 3.0 | hr | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel front temperature | 260 to 290 | °C | |
| Processing (melt) temperature | 280 | °C | |
| Mold temperature | 120 to 140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 3. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 4. DMS 1510/14 CFR 25.853 Appendix F Part 1, (a), 1, (i) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |