| About |
|---|
| Ixef® HC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance. Ixef® HC-1022 shows no evidence of cytotoxicity, sensitization, intracutaneous reactivity or systemic toxicity based on biocompatibility testing as defined by ISO 10993:1. Solvay offers these materials for healthcare applications that require limited exposure (less than 24 hours) to the body. Black: HC-1022 BK 000 Black: HC-1022 BK 001 Natural: HC-1022 NT 000 Gray: HC-1022 GY51 Additional colors available Custom colorable&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,Good Dimensional Stability,High liquidity,Good disinfection,Gamma radiation,E-beam disinfection,Biocompatible,Radioactive,Radiation disinfection,Solvent resistance,Low moisture absorption,Ethylene oxide disinfection |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.64 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.10 to 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Balance, 65% RH | 1.50 | Internal Method | |
| 23℃，24hr | 0.16 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 19500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 280 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.9 | % | ISO 527-2 |
| Bending modulus | 18500 | MPa | ISO 178 |
| bending strength | 380 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 110 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 850 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 1.5E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 0.50 to 1.5 | hr | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel front temperature | 260 to 290 | °C | |
| Nozzle temperature | 260 to 290 | °C | |
| Processing (melt) temperature | 280 | °C | |
| Mold temperature | 120 to 140 | °C | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Only Ixef® HC-1022 BK000 and Ixef® HC-1022 NT000 are ISO 10993 certified |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |